J9九游会体育

  • <tr id='xfrbk'><strong id='be3r3'></strong> <small id='ziuw1t'></small><button id='vrqwdy'></button><li id='zute6'> <noscript id='ppc05a'><big id='l8akmv'></big><dt id='fnaix'></dt></noscript></li></tr> <ol id='79uu'><option id='wif8jh'><table id='x4sn'><blockquote id='iij9'> <tbody id='oyjcj'></tbody></blockquote></table></option></ol><u id='re12zr'></u><kbd id='aetl'> <kbd id='pgd47'></kbd></kbd>

    <code id='ny2hw'><strong id='9z0zpt'></strong></code>

    <fieldset id='wbla'></fieldset>
          <span id='brhyk0'></span>

              <ins id='3n5ieg'></ins>
              <acronym id='m8o6f'><em id='fgn34a'></em><td id='914tt'><div id='0ffz'></div></td></acronym><address id='7cfg'><big id='ybi2'><big id='2hytd'></big><legend id='kz2pa'></legend></big></address>

              <i id='ojgura'><div id='jtwjr'><ins id='bi464d'></ins></div></i>
              <i id='8uat'></i>
            1. <dl id='vy5dz'></dl>
              1. <blockquote id='uqis2p'><q id='vcw9hf'><noscript id='a87kha'></noscript><dt id='t8clnp'></dt></q></blockquote><noframes id='fj7ao'><i id='baizup'></i>
                

                欢迎浏览我们的网站

                浙江百胜钢业

                致力于不锈钢管道的安全与可靠

                FOR PIPING SAFETY AND RELIABILITY

                全国免费咨询热线:

                15988016390

                当前位置: 首页 > 新闻资讯 > 行业新闻

                氮合金对不锈钢管强度的影响

                文章作者:admin 人气:发表时间:2021-07-26 09:21:24


                按照GB/T228-2002试验标准对试验不锈钢管进行热轧后的室温拉伸试验,热轧后试验钢的屈服强度和抗拉强度与固态相比有很大的提高。提高:屈服强度提高200MPa以上,至少760MPa;抗拉强度提高100MPa以上可达898MPa,最低1035MPa,最高1150MPa。在相同温度下,屈服强度和拉伸强度在40% 应变时最小,在60% 应变后在不锈钢管强度处达到最大值。

                不锈钢管强度的增加是由于变形引起的加工硬化。另一方面是晶界强化。热轧变形后,再结晶的发生增加了晶粒细化和晶界。晶界的主要作用是阻挡位错的运动,晶粒越细,晶界越多,阻挡位错滑移的作用越大,金属材料的屈服强度就越高。氮引起的晶界强化可能是晶粒细化的效果,或者可能是由于氮化物在晶界析出的钉扎效应。可以使用Hall-petch 公式计算这种加固。

                另一方面,在奥氏体不锈钢管中加入氮时,会产生很强的间隙固溶强化作用,从而大大提高了抗拉强度。与常规奥氏体不锈钢316L相比,氮合金奥氏体不锈钢管的屈服强度至少为760Mpa,达到898Mpa,而316L的屈服强度约为210Mpa,前者是后者的3-4倍。